Emanuel · 26th November 2006, 09:47 PM

Carlo and Saqr, thanks for your replies.

The short passage concerning this training exercise had merely stated that the sword would break -presumably on impact...I really don't recall its details but I will get the book from our library and read it again.

You're right about the angled leverage Carlo, and I understand it. Lateral stress can easily snap metal, one can even break some bars over one's head assuming proper training.
My thought was in regards to the discussion in this thread about wootz swords cutting through armour and chains. "If a sword were to snap on a direct edge impact with hard wood, how could it withstand metal?" I thought. But since we are talking of different swords for different purposes, the question is moot.

Emanuel

26th November 2006, 09:47 PM	#14
Emanuel Member Join Date: Jul 2005 Location: Toronto, Canada Posts: 1,242	Carlo and Saqr, thanks for your replies. The short passage concerning this training exercise had merely stated that the sword would break -presumably on impact...I really don't recall its details but I will get the book from our library and read it again. You're right about the angled leverage Carlo, and I understand it. Lateral stress can easily snap metal, one can even break some bars over one's head assuming proper training. My thought was in regards to the discussion in this thread about wootz swords cutting through armour and chains. "If a sword were to snap on a direct edge impact with hard wood, how could it withstand metal?" I thought. But since we are talking of different swords for different purposes, the question is moot. Emanuel