A vinegar bug in my head!!!!

katana · 25th June 2006, 06:23 PM

Would someone please explain the best way to vinegar etch a blade? Is a lemon Juice etch... a milder etch? (the Kris boys mention it occationally) Or stronger?

Rick · 25th June 2006, 06:51 PM

http://www.vikingsword.com/vb/showthread.php?t=2641

It may be just me but I recall Lemon bringing out a browner tone than Lime .

Flavio · 25th June 2006, 06:57 PM

Oooppsssss, i did it again, i play with your heart.....No, no stop!!!!!!

Here is another example: a salawar. Unfortunatly the very edge is quite pitted but anyway the result is nice

. I decide to stop also about african blade: I have rethought to the many pictures of the beginning of last century that shows many warriors of Central Africa with theirs shining swords and so i have decided to leave my african pieces as they are.

Katana, i think that the etching with vinegar is a gentle way, especially if you use the vinegar diluted with water (proportion 1 liter of vinegar : 2 of water) and cold (the process is faster if you heat the water).

katana · 25th June 2006, 07:07 PM

Thankyou Rick and Flavio, nice piece..

BSMStar · 27th June 2006, 01:13 PM

I have to caution you Flavio, that putting vinegar on everything is how I got addicted to fish and chip… and pickles.

Rick · 27th June 2006, 02:22 PM

That Khyber looks like monosteel with a hardened edge .

Here's a really topographic etch on my example (no I didn't do it) it came this way . Maybe mine looked like yours before it was so heavily etched .

Flavio · 27th June 2006, 03:55 PM

Hello Rick. No i think that you're right: mine is monosteel with hardened edge.

VANDOO · 27th June 2006, 04:28 PM

VINEGAR PHEWWWIE!!

VERY STINKIE , I PREFER LIME OR LEMON IT SMELLS SO MUCH BETTER, AND YOUR MOM MIGHT NOT MIND IT SO MUCH

25th June 2006, 06:51 PM	#2
Rick Vikingsword Staff Join Date: Nov 2004 Posts: 6,376	Last Post In This Thread http://www.vikingsword.com/vb/showthread.php?t=2641 It may be just me but I recall Lemon bringing out a browner tone than Lime .

25th June 2006, 06:57 PM	#3
Flavio Member Join Date: Dec 2004 Location: Italia Posts: 1,243	Oooppsssss, i did it again, i play with your heart.....No, no stop!!!!!! Here is another example: a salawar. Unfortunatly the very edge is quite pitted but anyway the result is nice . I decide to stop also about african blade: I have rethought to the many pictures of the beginning of last century that shows many warriors of Central Africa with theirs shining swords and so i have decided to leave my african pieces as they are. Katana, i think that the etching with vinegar is a gentle way, especially if you use the vinegar diluted with water (proportion 1 liter of vinegar : 2 of water) and cold (the process is faster if you heat the water). Attached Images

27th June 2006, 02:22 PM	#6
Rick Vikingsword Staff Join Date: Nov 2004 Posts: 6,376	That Khyber looks like monosteel with a hardened edge . Here's a really topographic etch on my example (no I didn't do it) it came this way . Maybe mine looked like yours before it was so heavily etched . Attached Images

25th June 2006, 06:23 PM	#1
katana Member Join Date: Jan 2006 Location: Kent Posts: 2,658	Would someone please explain the best way to vinegar etch a blade? Is a lemon Juice etch... a milder etch? (the Kris boys mention it occationally) Or stronger?

25th June 2006, 07:07 PM	#4
katana Member Join Date: Jan 2006 Location: Kent Posts: 2,658	Thankyou Rick and Flavio, nice piece..

27th June 2006, 01:13 PM	#5
BSMStar Member Join Date: Jan 2005 Location: Kansas City, MO USA Posts: 312	I have to caution you Flavio, that putting vinegar on everything is how I got addicted to fish and chip… and pickles.

27th June 2006, 03:55 PM	#7
Flavio Member Join Date: Dec 2004 Location: Italia Posts: 1,243	Hello Rick. No i think that you're right: mine is monosteel with hardened edge.

27th June 2006, 04:28 PM	#8
VANDOO (deceased) Join Date: Dec 2004 Location: OKLAHOMA, USA Posts: 3,138	VINEGAR PHEWWWIE!! VERY STINKIE , I PREFER LIME OR LEMON IT SMELLS SO MUCH BETTER, AND YOUR MOM MIGHT NOT MIND IT SO MUCH