Armoured breast plate ID please

Kmaddock · 21st November 2014, 04:56 PM

Hi All,
I appreciate the time you have all taken to reply to my enquiry.
As a new forum member who does not know a lot about such things I do not like always to be asking questions without giving much in the way of contributions.
Great to get a confirmation that my hunch was correct, I have some French armour form the 1830's and the difference in weight was what made me think this might be the genuine item, for the price of 2 take out pizzas I was prepared to gamble.

I have put up some pictures of the remnants of the studs and the mark on the neck for the sake of completion of the post, I do not think the mark will tell much as there is not a lot of definition.

I am not much into cleaning things beyond active rust, not laziness mind you, just I question too much restoration and patina removal. However, would it be wise to remove the varnish or just leave it as part of the history of the item, I have full access to any solvents and fume hoods as I work in chemistry so if you know of any good varnish removers please advise, di chloromethane would be my first choice but am open to suggestions.
Again thanks and regards
Ken

Ken Maddock · 21st November 2014, 06:14 PM

Last of pictures above is the indentation of the armoury mark on the neck of the breast plate, the proceeding ones are the inside of the breast plate showing the stud remnants, I used a triangle of paper to show the remnant on one side of the armour which is quiet small
Note the shinyness is all due to the varnish on the inside
Regards
Ken

A Senefelder · 21st November 2014, 08:12 PM

Ken, at this period armour of munitions quality like this were being produced in large quantities so the stamp at the neck line is as likely to be an armoury control mark as any sort of makers mark. As for cleaning it, that of course is your call but I left things as they were baring aggressive active rust on armour. If it was varninshed I left the varnish in place.

21st November 2014, 04:56 PM	#1
Kmaddock Member Join Date: May 2014 Location: Ireland Posts: 543	Hi All, I appreciate the time you have all taken to reply to my enquiry. As a new forum member who does not know a lot about such things I do not like always to be asking questions without giving much in the way of contributions. Great to get a confirmation that my hunch was correct, I have some French armour form the 1830's and the difference in weight was what made me think this might be the genuine item, for the price of 2 take out pizzas I was prepared to gamble. I have put up some pictures of the remnants of the studs and the mark on the neck for the sake of completion of the post, I do not think the mark will tell much as there is not a lot of definition. I am not much into cleaning things beyond active rust, not laziness mind you, just I question too much restoration and patina removal. However, would it be wise to remove the varnish or just leave it as part of the history of the item, I have full access to any solvents and fume hoods as I work in chemistry so if you know of any good varnish removers please advise, di chloromethane would be my first choice but am open to suggestions. Again thanks and regards Ken Attached Images

21st November 2014, 06:14 PM	#2
Ken Maddock Member Join Date: Aug 2013 Location: Ireland Posts: 104	Last of pictures above is the indentation of the armoury mark on the neck of the breast plate, the proceeding ones are the inside of the breast plate showing the stud remnants, I used a triangle of paper to show the remnant on one side of the armour which is quiet small Note the shinyness is all due to the varnish on the inside Regards Ken

21st November 2014, 08:12 PM	#3
A Senefelder Member Join Date: Jul 2009 Posts: 214	Ken, at this period armour of munitions quality like this were being produced in large quantities so the stamp at the neck line is as likely to be an armoury control mark as any sort of makers mark. As for cleaning it, that of course is your call but I left things as they were baring aggressive active rust on armour. If it was varninshed I left the varnish in place.