ThePepperSkull · 25th January 2012, 07:44 PM

^ With this in mind, Ideally how hot do i want my oven to be when I use this hilt removal method? Not over 200 celsius I'm guessing?

What if the kris has copper/silver inlay? Do those metals have a lower melting point and do I risk 'melting' them out of the blade? (I ask because I have a maranao blade with silver inlay that's attatched to an indonesian golok hilt. How the two got together is a mystery to me. I may leave it as-it because it's interesting though. And I don't have a kris hilt handy to go with it)

Battara · 25th January 2012, 11:26 PM

If you do it with low heat the inlay will be fine. If you use a blow torch, then BE VERY VERY CAREFUL since it could have the heat (like an acetalyne or map gas torch) to melt the inlays.

Rick · 25th January 2012, 11:26 PM

I would not put any edged weapon in a 392f oven .

This whole idea scares the daylights out of me .

Much safer, IMO, to apply heat to the base of the blade where temper/hardness is not as important .

No torches !!

ThePepperSkull · 26th January 2012, 04:54 AM

^ Would a hair dryer be enough to loosen the pitch or would a heat gun be needed?

fspic · 1st February 2012, 01:23 AM

You could try applying a large copper soldering iron against it as the heat would be lower and possibly enough would flow off to warm the resin. It would have to be applied several times but it would be under control.

25th January 2012, 07:44 PM	#1
ThePepperSkull Member Join Date: Aug 2009 Posts: 338	^ With this in mind, Ideally how hot do i want my oven to be when I use this hilt removal method? Not over 200 celsius I'm guessing? What if the kris has copper/silver inlay? Do those metals have a lower melting point and do I risk 'melting' them out of the blade? (I ask because I have a maranao blade with silver inlay that's attatched to an indonesian golok hilt. How the two got together is a mystery to me. I may leave it as-it because it's interesting though. And I don't have a kris hilt handy to go with it) Last edited by ThePepperSkull; 25th January 2012 at 08:01 PM.

25th January 2012, 11:26 PM	#2
Battara EAAF Staff Join Date: Dec 2004 Location: Louisville, KY Posts: 7,272	If you do it with low heat the inlay will be fine. If you use a blow torch, then BE VERY VERY CAREFUL since it could have the heat (like an acetalyne or map gas torch) to melt the inlays.

25th January 2012, 11:26 PM	#3
Rick Vikingsword Staff Join Date: Nov 2004 Posts: 6,336	I would not put any edged weapon in a 392f oven . This whole idea scares the daylights out of me . Much safer, IMO, to apply heat to the base of the blade where temper/hardness is not as important . No torches !!

26th January 2012, 04:54 AM	#4
ThePepperSkull Member Join Date: Aug 2009 Posts: 338	^ Would a hair dryer be enough to loosen the pitch or would a heat gun be needed?

1st February 2012, 01:23 AM	#5
fspic Member Join Date: May 2010 Posts: 27	You could try applying a large copper soldering iron against it as the heat would be lower and possibly enough would flow off to warm the resin. It would have to be applied several times but it would be under control.