[GIO]

Originally Posted by David

Yes, Jagabuwana's very well presented post on staining with sulphur and rice water is probably the closest alternative i've seen to a good staining with warangan.
I did note that you titled this thread "Staining a Balinese Blade". Jaga is showing his process on an old Bugis blade with a fairly topographical surface. So i'm not sure what sulphur and rice water will do to the smooth, polished surface we find on most Bali keris.

In fact, after processing a polished blade with sulphur and rice water (and salt if you like), we can observe that iron appears corroded, while iron/nickel resists much better. In my experience, even polished Bali blades become rough after this treatment. The effect obviously is related to the length of immersion.

[David]

Originally Posted by GIO

In fact, after processing a polished blade with sulphur and rice water (and salt if you like), we can observe that iron appears corroded, while iron/nickel resists much better. In my experience, even polished Bali blades become rough after this treatment. The effect obviously is related to the length of immersion.

Thanks Gio, that is what i was curious about since the surface of the example Jagabuwana showed did indeed look somewhat eroded. I would not want a Bali keris to get this kind of surface if it indeed started with a polished blade.

[Anthony G.]

Originally Posted by David

Thanks Gio, that is what i was curious about since the surface of the example Jagabuwana showed did indeed look somewhat eroded. I would not want a Bali keris to get this kind of surface if it indeed started with a polished blade.

That is why I dare not try becos my bilah is polished smooth and expensive.

[David]

Originally Posted by Anthony G.

That is why I dare not try becos my bilah is polished smooth and expensive.

Can you post a photo of it?

[jagabuwana]

It's worth noting that the corrosion that you can see on the blade that I shared was not due to the sulphur treatment.

From my eyeballing, the blade didn't appear to get worse after this treatment, compared to how it was before. Something that I have noticed and has been difficult for me to control is the appearance of brightly rust-looking patches on the blade after a sulphur treatment. It's easy enough to remove with a brush, water and detergent, but this also removes some of the staining.

But I can understand why you would be reluctant to do this on a blade that you value, or one that you would otherwise not want to treat in this way.

[Anthony G.]

Originally Posted by jagabuwana

It's worth noting that the corrosion that you can see on the blade that I shared was not due to the sulphur treatment.

From my eyeballing, the blade didn't appear to get worse after this treatment, compared to how it was before. Something that I have noticed and has been difficult for me to control is the appearance of brightly rust-looking patches on the blade after a sulphur treatment. It's easy enough to remove with a brush, water and detergent, but this also removes some of the staining.

But I can understand why you would be reluctant to do this on a blade that you value, or one that you would otherwise not want to treat in this way.

I think i probably will use this method on old average keris but not new keris
Thanks for sharing.