Default Citric soak

Question, will a citric acid soak damage or remove or affect gold work?
Gavin Nugent is offline   Reply With Quote
Old 24th July 2014, 06:33 PM   #2
Henk
Member
 
Henk's Avatar
 
Join Date: Dec 2004
Location: The Netherlands
Posts: 1,209
Default

Follow this link and go to post nr. 4. There you will find the answer given by Alan Maisey.
http://www.vikingsword.com/vb/showthread.php?t=18733
Henk is offline   Reply With Quote
Old 24th July 2014, 07:27 PM   #3
Gavin Nugent
Member
 
Gavin Nugent's Avatar
 
Join Date: Oct 2007
Posts: 2,818
Default

Thank you Henk, I will refrain from soaking.

Best regards

Gavin
Gavin Nugent is offline   Reply With Quote
Old 24th July 2014, 10:07 PM   #4
Sajen
Member
 
Sajen's Avatar
 
Join Date: Aug 2007
Location: Germany, Dortmund
Posts: 8,408
Default

I think that you can't say it for global. When rust is under the gold migrated I never would soak a blade in citic acid but when the gold is firmley attached nothing will happen, this is the experience I have had with blades I have cleaned with citric acid.

Regards,
Detlef
Sajen is offline   Reply With Quote
Old 25th July 2014, 03:41 AM   #5
Gavin Nugent
Member
 
Gavin Nugent's Avatar
 
Join Date: Oct 2007
Posts: 2,818
Default

Thank you Detlef. I will approach the blade with a more hands on approach when time permits and if the gold looks safe I'll deliver a final etch at the end.
Gavin Nugent is offline   Reply With Quote
Old 25th July 2014, 08:48 AM   #6
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

Yes Detlef, I agree totally, that is why I wrote:-

"---That gold may not get through a soak---"

I have found that the most reliable way in which to find out if the gold is firmly attached is to go ahead and soak the blade in some sort of acidic bath:- if the gold is still in place on the blade when you take it out of the bath you can bet that it is firmly attached.

But jokes aside, with any gold on blades, especially the sort gold we find on keris blades, it is best to be super cautious. It can sometimes be a good idea to clean mechanically first, then follow up with very selective and cautious brushing of the acidic medium.

Another way to tackle the problem of cleaning gold ornamented blades is to paint over the gold with nail polish, but this is not recommended unless the gold does look to be pretty secure. The polish comes off easily enough with acetone.

Last edited by A. G. Maisey; 25th July 2014 at 09:49 AM. Reason: correct text
A. G. Maisey is offline   Reply With Quote
Old 25th July 2014, 11:01 AM   #7
Sajen
Member
 
Sajen's Avatar
 
Join Date: Aug 2007
Location: Germany, Dortmund
Posts: 8,408
Default

Quote:
Originally Posted by A. G. Maisey
I have found that the most reliable way in which to find out if the gold is firmly attached is to go ahead and soak the blade in some sort of acidic bath:- if the gold is still in place on the blade when you take it out of the bath you can bet that it is firmly attached.
Sajen is offline   Reply With Quote
Old 25th July 2014, 11:05 AM   #8
Sajen
Member
 
Sajen's Avatar
 
Join Date: Aug 2007
Location: Germany, Dortmund
Posts: 8,408
Default

Quote:
Originally Posted by A. G. Maisey
But jokes aside, with any gold on blades, especially the sort gold we find on keris blades, it is best to be super cautious. It can sometimes be a good idea to clean mechanically first, then follow up with very selective and cautious brushing of the acidic medium.

Another way to tackle the problem of cleaning gold ornamented blades is to paint over the gold with nail polish, but this is not recommended unless the gold does look to be pretty secure. The polish comes off easily enough with acetone.
Yes, I agree with you. I have cleaned once a blade with gold by brushing the blade carefully with fresh opened lemons which I have bought in an asia shop.

Regards,
Detlef
Sajen is offline   Reply With Quote
Old 25th July 2014, 02:07 PM   #9
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

Something has occurred to me with all this talk about "gold on blade" business.

We haven't said how the gold is attached to the blade.

Without straining the brain cells too hard I can think of 4 ways that gold is put onto a blade:-

old fashioned fire gilding

attached with natural resin --- or in the modern age with a commercial adhesive

mechanical attachment by roughening the surface and hammering the gold over the design set out by roughening (koftgari)

mechanical attachment where an undercut cavity is cut into the blade surface, a lump of gold is hammered into the cavity so that the gold enters the undercuts, and leaves a large lump of gold above the surface of the blade, then that gold is carved. Effectively this is inlay, in the case of Indonesian blades, inlay that is sometimes very exaggerated.

If the gold is old fashioned fire gilding it is not a good idea ever to soak the rusty blade in an acidic medium

If the gold is attached by resin or other adhesive the decision to soak or not depends upon the degree of corrosion:- if there is a good chance that the rust has penetrated beneath the surface of the adhesive, you do not soak; if the rust is just a light surface dusting you brush with acid. In between these two extremes your experience guides you with the right way to go.

With typical Indian koftgari gold attachment I would never, ever soak, nor try to remove rust with an acidic medium in any way. Far better to conserve and live with the russetted surface. However, with good quality kinatah work, which is similar to koftgari work, the gold is often quite heavy and the attachment is robust. I would always think a number of times before I soaked a blade like this, even though it might not lose any gold, but I would not hesitate to clean by brushing with an acidic medium.

Where the gold has been attached by hammering into a dove-tailed hole in the blade, cautious soaking and careful brushing are both possible. Even if the gold carving works loose from the cavity, modern adhesives permit undetectable replacement.

In fact, I personally regard soaking as a "lazy-man's" way of cleaning blades. Yeah, sure I've used it and used it many times, but I do not believe it is the best way to clean any blade, including keris. I do believe that painstaking mechanical cleaning followed by careful acidic brushing is probably the best way to clean the blades of S.E.Asia.

I have read of other methods where electric current is used, but I have no knowledge nor experience of these methods. From what I have heard, cleaning in this way might well be superior to the traditional methods that I know.
A. G. Maisey is offline   Reply With Quote
Old 25th July 2014, 06:51 PM   #10
Sajen
Member
 
Sajen's Avatar
 
Join Date: Aug 2007
Location: Germany, Dortmund
Posts: 8,408
Default

Quote:
Originally Posted by A. G. Maisey
In fact, I personally regard soaking as a "lazy-man's" way of cleaning blades. Yeah, sure I've used it and used it many times, but I do not believe it is the best way to clean any blade, including keris. I do believe that painstaking mechanical cleaning followed by careful acidic brushing is probably the best way to clean the blades of S.E.Asia.
Very good said! And again my full agreement.
Sajen is offline   Reply With Quote
Old 25th July 2014, 07:03 PM   #11
David
Keris forum moderator
 
David's Avatar
 
Join Date: Aug 2006
Location: Nova Scotia
Posts: 7,012
Default

Quote:
Originally Posted by A. G. Maisey
Even if the gold carving works loose from the cavity, modern adhesives permit undetectable replacement.
Alan, is there a particular modern adhesive you would recommend for such repair?
David is offline   Reply With Quote
Old 25th July 2014, 11:27 PM   #12
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

The "gold-back-into-hole" job?

My personal favourite adhesive for anything like this is Araldite, its a two part epoxy glue. There is a version that sets within 5 minutes, and another one that sets overnight --- they say an hour, but it only sets in an hour in warm to hot weather.

The surfaces need to be roughened up a little and be very clean and free from any grease, acetone is good for this, and the job needs to be firmly clamped while the stuff sets.

Not clamped to the point where the adhesive gets squeezed out, but just a good firm pressure. With the 5 minute stuff you can just hold it tight with your fingers while it sets.

Once set, but not cured, you trim off the excess with a sharp blade. You can also wash off barely set excess with water, and set excess with acetone, but I have seen jobs come adrift if too much of the fluid is used, or too little care is used, its safer to let it just set up firm, then trim. You can only get as neat as you can see, so bright light and magnification is essential.

In Indonesia they use one of the 'super-glues' for anything like this, but these adhesives dry out after a while, usually a few years, and everything comes loose and you can lose little bits. This is particularly true of the stones in mendak and selut --- if its an old mendak or selut and had stones replaced in Jawa you can bet its been done with Alteco (a super-glue); eventually the glue will give way and you'll lose a stone, and rose cut rock crystal is not all that easy to find outside Jawa --- even in Jawa its not that easy any more. If the stone is a rose cut diamond its even more difficult to get one.

Sorry for the long answer.

Short answer:- Araldite.
A. G. Maisey is offline   Reply With Quote
Old 26th July 2014, 05:28 AM   #13
Shakethetrees
Member
 
Shakethetrees's Avatar
 
Join Date: Apr 2014
Location: Louisiana
Posts: 363
Default

Mr. Maisey's advice is excellent!

I have professionally restored blades (and other antique metalwork) for about thirty years. I had the opportunity to participate in a workshop taught by a Western metal smith and his Japanese trained wife whose names I forget just now, both acknowledged masters in their craft. My experience has been with mostly American and European blades, but with some Asian work as well.

I have done a little inlay from scratch as well as restored "around" it and over it depending on the type, or not at all.

Fire gilt decoration on blades is completely fugitive, so the smart thing is to stay away unless the problem endangers the blade to the point where a percentage of sacrificed gilding is a necessary cost in order to preserve the life of the whole.

Likewise with koftghari--too delicate to risk.

I have never run across any gold adhered by an organic adhesive, unless it's on a modern blade, something I usually do not fool with.

A restorer's dream is a blade mounted with undercut secured inlay, I believe the Japanese terms are sen zogan for line inlay, hira zogan for two dimensional inlay. I have rarely seen these last two come loose, but if the inlay is flush with the surface and pure gold (not low karat alloy) it can be carefully tapped into place, spreading the gold into any voids, locking it mechanically and securely. But, I emphasize pure gold only, and very light tapping using the end grain of a hardwood dowel specially shaped for the purpose.

If you have any doubt about your abilities, or any other reservations, leave it alone.
Shakethetrees is offline   Reply With Quote
Old 26th July 2014, 08:47 AM   #14
max
Member
 
Join Date: May 2010
Posts: 12
Default rust and gold

As you can see the rust lay's between the gold pieces
Attached Images
  
max is offline   Reply With Quote
Old 26th July 2014, 11:19 PM   #15
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

Yes Max, correct, gold does not rust.

But underneath that gold is iron or steel and that does rust.

What often happens is that over time the rust penetrates to the iron under the gold, and the only thing supporting the gold is rust. The acidic soak also penetrates under the gold and weakens the rust.

My most important lesson came when I saw a highly respected m'ranggi in Solo take a blade out of an acidic soak. When it went into the soak it had been a very beautiful kinatah blade with probably better than 90% of the gold intact; when it came out of the soak it had maybe 20% of the gold still on the blade.

Mechanical clean first, if possible follow-on with an acidic brushing.

Best not to soak.
A. G. Maisey is offline   Reply With Quote
Old 27th July 2014, 04:28 PM   #16
GIO
Member
 
GIO's Avatar
 
Join Date: Dec 2009
Posts: 310
Default

Quote:
Originally Posted by A. G. Maisey
I have read of other methods where electric current is used, but I have no knowledge nor experience of these methods. From what I have heard, cleaning in this way might well be superior to the traditional methods that I know.
I did used the electric system to remove rust. It works but long lasting treatment is required. I think that it would work with kinatah.
Gio

You can use a 12V car battery. The liquid is a NaOH solution.
The process may take 12 - 24 hours with no risk of damage. Only the rust will be removed.
Attached Images
 
GIO is offline   Reply With Quote
Old 27th July 2014, 10:00 PM   #17
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

Thanks Giovanni.

If it also removes the rust that is underneath the gold, then that would trouble me, because with old kinatah it is only the rust that is holding the kinatah in place. With kinatah we need to remove the surrounding rust and not disturb what is under the kinatah.

I do think this electric method might be better for a plain steel blade though.
A. G. Maisey is offline   Reply With Quote
Old 27th July 2014, 10:52 PM   #18
drdavid
Member
 
Join Date: Aug 2005
Location: Australia
Posts: 369
Default

Hi Gio
what strength NaOH have you used in this set up
what sort of wire are you using in the coils, copper?
regards
DrDavid
drdavid is offline   Reply With Quote
Old 2nd August 2014, 01:21 PM   #19
Gavin Nugent
Member
 
Gavin Nugent's Avatar
 
Join Date: Oct 2007
Posts: 2,818
Default

Thank you all for an interesting insight.

Soaks and such have been noted throughout various threads that they take better with heat...is this true of the citric soaking? With some steel and specialist chemicals I have personally seen some benefit in this but I ask also for economy too (saving product)...I am thinking, as the citric soak is not a harsh chemical, of keeping the required pine apple juice or other mix I may make in the fridge, encapsulated in capped PVC tubing for longevity and actually soak blades in the tube in the fridge...just something I have been pondering...does anyone have any experience with such notions?

With thanks
Gavin Nugent is offline   Reply With Quote
Old 4th August 2014, 11:53 AM   #20
GIO
Member
 
GIO's Avatar
 
Join Date: Dec 2009
Posts: 310
Default

Quote:
Originally Posted by drdavid
Hi Gio
what strength NaOH have you used in this set up
what sort of wire are you using in the coils, copper?
regards
DrDavid
Hi David
Please apologize for my late answer, but a thunderstorm has put out of order my phone line and burnt my modem. Only this morning all has been repaired,
As to the electric de-rusting, my plant is not exactly what recommended in the book, but it works.
I use a rectangular plastic flower pot, on the floor of which I have put a serpentine of iron wire (about 1,5 mm thick). The quantity of NaOH is 1 - 2 tea cups per 5 litres (I think that the concentration has some influence on the time required for cleaning). The rheostat is needed for starting the reaction with a low voltage, increasing it slowly. I do not have a rheostat and I use a car light bulb to avoid a short circuit. The power comes from a 12 V car battery charger. Obviously the piece to be treated should not touch neither the iron wire. I suspend it with some pieces of plastic.
When the reaction starts, I can eliminate the bulb, and the reaction becomes more violent, but I prefer to leave the bulb in the circuit to avoid any risk, particularly when the system is unattended. Of course the current is lower and time needed is higher.
When the process ends the piece is black and it needs to be brushed to eliminate all the transformed rust.
When I am back home (beginning September) I shall send you the original text (from a French book: "Restauration des armes ŕ feu"). If you have any doubts please feel free to contact me again.

Alan
Yes, I agree with you: any de-rusting treatment is very risky to kinatah if the iron is heavily rusted. If the rust is light and has not yet developed under the gold foil the treatment is safe, but always great attention is needed.
GIO is offline   Reply With Quote
Old 4th August 2014, 02:22 PM   #21
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

Thanks for your additional comment Giovanni.

Where the kinatah work is only gold foil I would be reluctant to touch it with just about anything, even when it looks good and not heavily rusted, but there is also much heavier kinatah work that uses either very heavy gold over an iron carved figure, or heavy carved gold. With this type of work I believe your electric method could be fairly safe with any except the worst of corrosion.
A. G. Maisey is offline   Reply With Quote
Old 15th September 2014, 11:31 AM   #22
GIO
Member
 
GIO's Avatar
 
Join Date: Dec 2009
Posts: 310
Default

Quote:
Originally Posted by drdavid
Hi Gio
what strength NaOH have you used in this set up
what sort of wire are you using in the coils, copper?
regards
DrDavid
Hi David,
I have made a free but faithful translation of the original text about electric de-rusting (from "Restauration des armes ŕ feu" by Jean-René Clergeau, Stampfli & Cie, Berne 1981)

Electrolysis
This procedure is based upon the reduction of oxides through direct current.
This is carried out in a container for electrolysis where the piece to be de-rusted is the cathode. It is easy to find the necessary material, the more expensive component is a 6 or 12 V car battery charger. The cylindrical container can be of any insulating material (ceramic or plastic-which is better) of a convenient size. For keris cleaning a height of 70/80 cm and a width of 20 cm can be utilized for any size, including Panjang.
The anode is made with an iron bar, of the type used for concrete, 6-8 mm thick, made up in a spiral against the internal wall of the container. At an end the positive pole is connected, while the negative pole is connected with the piece to be treated through a non-galvanized iron wire. The piece must be fully submersed and should not touch neither the bottom of the container nor the anode. The electrolyte is a solution in water (better rain water-I use distillate water used for batteries) of caustic soda in granules in the proportion of 50 grams per litre. This solution shall be filtered from time to time, and the anode cleaned.
On the positive thread a rheostat should be inserted, so that the electric power can be reduced, mainly for starting the reaction, so that the battery charger is not unnecessarily strained. A buzzer can be useful for indicating a surcharge. The sound will warn to reduce the power, and increase it as soon as the electrolyse process starts , demonstrated by the appearance of hydrogen bubbles (this happens quickly). The operation must be left working for 12 to 24 hours, but a longer period is allowed.
The blade, once the process ends, will show a blackish surface of reduced oxides, which must be eliminated with washing and brushes (of bronze, if necessary), until the metal appears clean and brilliant.
CAUTION: THIS PROCEDURE MUST NOT BE USED FOR SPRINGS WHICH BECAME BRITTLE (luckily our keris do not have springs), AND A GREAT ATTENTION SHOULD BE PAID IN CASE OF KINATAH ON VERY RUSTED BLADES.
The illustration transmitted last month should help.
I hope you will find such information useful
GIO is offline   Reply With Quote
Old 15th September 2014, 12:23 PM   #23
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

Why did the springs become brittle?

Difference between a spring and other ferric material is that the spring has been hardened and then the temper has been drawn.

A weapon is heat-treated in the same way, that is, it has been heat treated and often the temper that it has been drawn to is the same as a spring.

A keris is also heat treated, but with a keris, because of the laminate construction probably only the hardened edges of the core will react in the same way as a spring, ie, they must become brittle.

After reading this I would hesitate to use electric rust removal on any keris except perhaps the old junky corroded ones that have lost any hardened material long ago. I would not use this treatment on any keris that I valued.
A. G. Maisey is offline   Reply With Quote
Old 15th September 2014, 03:57 PM   #24
GIO
Member
 
GIO's Avatar
 
Join Date: Dec 2009
Posts: 310
Default

[QUOTE=A. G. Maisey]Why did the springs become brittle?

QUOTE]

Good question, Alan
I am not in a position to answer. I only report what is indicated in the book I mentioned.
In my very humble opinion, the heat treatment ("temper") of a keris is far from the procedure needed to harden a spring, both for what the heat needed and for the partial section of the blade which is interested. In fact a keris blade can be easily bent, and this should not happen easily in case the steel iron core is tempered. It is true that also Japanese katanas can be bent, and this could be due to the fact that different types of steel are layered to form the blade, and different percentages of carbon should be differently treated (different temperature of the heating and of the water), and the keris is made in a similar way as the katanas.
Always in my very humble opinion the heat treatment of a keris is intended more to eliminate tensions in the metal due to the hammering than to harden the blade.
I repeat that I know nothing about these matters and should be very grateful if some more prepared friend would contribute and give a competent opinion.
GIO is offline   Reply With Quote
Old 15th September 2014, 05:43 PM   #25
Emanuel
Member
 
Emanuel's Avatar
 
Join Date: Jul 2005
Location: Toronto, Canada
Posts: 1,242
Default

Quote:
Originally Posted by A. G. Maisey
Why did the springs become brittle?
Rust removal through electrolysis is subject to hydrogen embrittlement: http://en.wikipedia.org/wiki/Hydrogen_embrittlement

Hydrogen evolved from the water through the electrolytic process can fuze with the object and induce cracking. Low-alloy, medium/high carbon steels like spring steels are apparently very susceptible to this.

Reversing the hydrogen absorption is done through heating.

There's never any quick solution I guess.

Emanuel
Emanuel is offline   Reply With Quote
Old 16th September 2014, 09:45 AM   #26
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

Re heat treat.

For simple forge heat treat, the heat treatment of a spring and a blade is the same, the only variation is the colour to which it may be drawn, and even that does not always vary.

In simple terms, after annealing, you heat the object to be hardened to critical, which can be most easily detected by testing with a magnet:- when the magnet does not grip the object it is at critical temperature.

The object, either blade or spring is then plunged into the cooling medium, which may be water, or oil, or brine, dependent upon the steel to be hardened.

After the hardening the temper is drawn. There are a number of various indicators used by traditional blacksmiths to gauge the correct temperature, for a spring, some old timers would run a piece of hardwood down the object and gauge the temperature by the colour and character of the sparks thrown off.

The usual textbook method is to clean off the surface to be drawn, and re-heat the object until the correct colour for intended hardness shows, then cool the object again in the cooling medium.Different levels of hardness are required for different purposes.

As noted, a keris blade, and many other blades, are laminated, and in the case of a keris, only the projecting edges of the blade core are homogenous steel, the laminations that sandwich the core are irons of various qualities, or iron + nickelous material. This is the reason I wrote:-

A keris is also heat treated, but with a keris, because of the laminate construction probably only the hardened edges of the core will react in the same way as a spring, ie, they must become brittle.

The heat treat of a keris blade is not done to relieve any tensions.

The blade would be annealed to relieve tensions, not subjected to a heat-treat to relieve tensions.

However, a keris blade is carved from a forged blank (bakalan):- most of what we see in the blade is produced by stock removal, and during this process the blade may have been returned to the forge several times prior to heat-treat. By the time it actually gets to heat-treat stage there is probably not much, if any, tension to relieve. Put it another way:- I've made a few keris and a whole heap of damascus and plain carbon steel blades. I always annealed the damascus and the carbon steel, I never annealed any of the keris I made.

Some keris blades can be bent, but not necessarily all --- or more precisely, not necessarily all blades can be bent in the hardened section of blade; since hardening of a keris is only for part of the length of the blade, they can all be bent in the unhardened section.

The temper is not drawn in a keris blade, it is simply plunged point first into the cooling medium. End of story. If the laminations are the traditional irons or iron and nickel, yes, you can bend the hardened section of the blade a little without too many concerns, however, if steel has been used as a laminate material it may or may not bend.

In the damascus blades that I made I did not draw the temper in small blades, like trout/bird blades, but in other larger blades that could conceivably be used for chopping I did draw the temper. The reason I did this was because the small blades were intended only to cut, and if the temper was not drawn the edge would last longer, but the bigger blades that might be used to chop could gap if the temper was not drawn, and that edge would not hold as long as the small blade edge.

Emanuel has given us a link to additional information as to exactly why this cracking can occur. I do not fully understand what I've read, but I think it comes down to :- ferric material that is hard is susceptible to cracking. Ferric material that is not hard is not susceptible to cracking. But I am unclear as to whether it is the quality of hardness, or the content of carbon that leads to this susceptibility.

In any case, it seems that an old, degraded keris would be quite safe to de-rust using electricity, but a well preserved good quality keris would be at high risk.
A. G. Maisey is offline   Reply With Quote
Old 16th September 2014, 11:13 PM   #27
A. G. Maisey
Member
 
Join Date: May 2006
Posts: 6,675
Default

It has occurred to me that some of what I have written in the preceding post could be clarified.

The photos are of my desk knife. It is 01 damascus, I made it about 30 years ago --- in fact, it was the first piece of damascus I made, it was intended to be a 10inch bowie, but it was full of faults that I kept on removing until I finished up with a desk knife.

It has been given a spring temper, that is, it was hardened and drawn to a full blue. This means that it is pretty hard, holds an edge very well and will bend and return to dead straight.

The link will take you to a page that explains the colours that we use as a guide for drawing a temper.

http://www.anvilfire.com/article.php...s_hardness.htm
Attached Images
  
A. G. Maisey is offline   Reply With Quote
Old 24th September 2014, 11:13 AM   #28
kulbuntet
Member
 
kulbuntet's Avatar
 
Join Date: Oct 2008
Location: Amsterdam, Netherlands
Posts: 159
Default

oxalic acid is a mild acid that work really good for removing rust.
kulbuntet is offline   Reply With Quote
Reply

Thread Tools Search this Thread
Search this Thread:

Advanced Search
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT +1. The time now is 01:46 PM.


Powered by vBulletin® Version 3.8.11
Copyright ©2000 - 2024, vBulletin Solutions Inc.
Posts are regarded as being copyrighted by their authors and the act of posting material is deemed to be a granting of an irrevocable nonexclusive license for display here.