damage keris tip

[A. G. Maisey]

I'm sorry Anthony, but the tip picture is very unclear, I need to be able to see clearly the degree that this tip is bent, and how it is bent.

However, like Kai, I doubt that this blade has been hardened, if it was hard, the point should have broken off; if it was hardened there should be a reasonably obvious colour change that would be visible in the projecting edge of the core. I can see no colour difference at all.

See if you can do a better close up photo, I cannot see enough in this one.

I need to see the blade from the edge and I need to confirm that there is in fact no metal missing from the tip.

[Anthony G.]

Originally Posted by A. G. Maisey

I'm sorry Anthony, but the tip picture is very unclear, I need to be able to see clearly the degree that this tip is bent, and how it is bent.

However, like Kai, I doubt that this blade has been hardened, if it was hard, the point should have broken off; if it was hardened there should be a reasonably obvious colour change that would be visible in the projecting edge of the core. I can see no colour difference at all.

See if you can do a better close up photo, I cannot see enough in this one.

I need to see the blade from the edge and I need to confirm that there is in fact no metal missing from the tip.

i tried to take many photo but results are bad. I took this photo which slightly tilted. hope it helps.

[mariusgmioc]

Hello Anthony,

Like you, I like my blades to be in perfect condition. Unfortunately, nothing is perfect...

I had exactly the same problem with a few kerises (but also with other blades) I got in some auctions.
In all situations, I managed to repair the blades myself, so that the repairv is practically invisible to the naked eye or even under magnifying glass examination.

What I did, was:
1. straighten up the bent tip with pliers and/or gentle hammering with a very light hammer
2. very light & fine polishing of the very tip (this means just 0.5-2 mm, precisely at the bent area)
3. apply very diluted etchant (I used very diluted Nital, because that was the only etchant I had but I assume that even instant coffee will do the job) to the very tip until it gets exactly the same patina like the rest.

Unfortunately, in most cases, during step 1 the bent material broke off.
Then:
2a. reshape the tip with a very fine file, then do steps 2 and 3 from above.

I have absolutely no idea if what I did was right, but certainly the results were always very good (at least to my eyes). I am just a mechanical engineer and have no special blade-working skills, so I assume that almost everybody can do what I did.

I am very curious to read what other fellows here have to say about this.

Well, anyhow don't get too upset because as Alan said it is nothing that can't be fixed easily.


PS: I found this happening quite often with keris blades, probably because the relatively softer material of the blades.

PPS: Very beautiful pamor. Why don't you show us the whole blade?
The brownish patination near the tip is not very visible and I wouldn't bother, but if you are bothered you can try and clean it with WD40, applied stricly there with a toothpick and some wrapped cotton. My two cents.

[Anthony G.]

Originally Posted by mariusgmioc

Hello Anthony,

Like you, I like my blades to be in perfect condition. Unfortunately, nothing is perfect...

I had exactly the same problem with a few kerises (but also with other blades) I got in some auctions.
In all situations, I managed to repair the blades myself, so that the repairv is practically invisible to the naked eye or even under magnifying glass examination.

What I did, was:
1. straighten up the bent tip with pliers and/or gentle hammering with a very light hammer
2. very light & fine polishing of the very tip (this means just 0.5-2 mm, precisely at the bent area)
3. apply very diluted etchant (I used very diluted Nital, because that was the only etchant I had but I assume that even instant coffee will do the job) to the very tip until it gets exactly the same patina like the rest.

Unfortunately, in most cases, during step 1 the bent material broke off.
Then:
2a. reshape the tip with a very fine file, then do steps 2 and 3 from above.

I have absolutely no idea if what I did was right, but certainly the results were always very good (at least to my eyes). I am just a mechanical engineer and have no special blade-working skills, so I assume that almost everybody can do what I did.

I am very curious to read what other fellows here have to say about this.

Well, anyhow don't get too upset because as Alan said it is nothing that can't be fixed easily.


PS: I found this happening quite often with keris blades, probably because the relatively softer material of the blades.

PPS: Very beautiful pamor. Why don't you show us the whole blade?
The brownish patination near the tip is not very visible and I wouldn't bother, but if you are bothered you can try and clean it with WD40, applied stricly there with a toothpick and some wrapped cotton. My two cents.

Thank you for your kind words.

[mariusgmioc]

Thank you for the photo!

I love to see beautiful blades, so more photos... please!

Lovely pamor!

[Anthony G.]

Originally Posted by mariusgmioc

Thank you for the photo!

I love to see beautiful blades, so more photos... please!

Lovely pamor!

Here you go.
http://www.vikingsword.com/vb/showthread.php?t=24903

[mariusgmioc]

Originally Posted by Anthony G.

Here you go.
http://www.vikingsword.com/vb/showthread.php?t=24903

Thanks! Lovely blade!

[asomotif]

Originally Posted by Anthony G.

i tried to take many photo but results are bad. I took this photo which slightly tilted. hope it helps.

And from the other side of the blade ?

I am interested to know what Alan will advise when we have the complete picture.

[Anthony G.]

Originally Posted by asomotif

And from the other side of the blade ?

I am interested to know what Alan will advise when we have the complete picture.

The other side of the bilah is the same. I will have to take the photo during weekend where it is better to take the photo during normal daytime. The photo will be clearer.