[mariusgmioc]

Hello Roland,

Can you please substantiate the asertion that Tutankhamon's blade was differentially hardened?

Regards,

Marius

PS: I attach a couple of example of blades that display a difference in oxidation around the edge and are NOT differentially hardened (if you take a Magbetu knife from the photos below and clean a little bit more the forging oxidation from the surface of the blade, you may end up exactly with the type of visual effect you noticed on Tutankhamon's blade).

[Roland_M]

Originally Posted by mariusgmioc

Hello Roland,

Can you please substantiate the asertion that Tutankhamon's blade was differentially hardened?

Regards,

Marius

Hello Marius,

I can only judge by the pictures, I never had King Tuts dagger in my hands.

But almost every picture of this particular dagger shows a brighter area around the edges, which is normally a sign for a complex heat treatment.

King Tuts dagger is fully polished, your examples only have a grinded/polished cutting edge, typical for Africa. The upper curved blades are artificially blackened.

To be 100% sure, I need to polish and etch this dagger .

My personal theory is very simple. I believe, that there was a unknown sophisticated culture like the fictional Atlantis, which brought the knowledge to Egypt and other parts of the world.


Regards,
Roland