SURPRISE! Wootz Steel in a Most Unexpected Place!...An Aceh Podang/Peudueng

[asomotif]

Originally Posted by CharlesS

I would be most interested in seeing examples of other original peudeung scabbards to give me some ideas to go by in completing this wooden one. Thanks for any pics here.

Finally took some pictures with acceptable daylight of a peudeung from my own collection. Scabbard leather over wood.
Blade is laminated, What would you call this blade ?

Best regards,
Willem

[Sajen]

Originally Posted by asomotif

Finally took some pictures with acceptable daylight of a peudeung from my own collection. Scabbard leather over wood.
Blade is laminated, What would you call this blade ?

Best regards,
Willem

Hello Willem,

I would call it a pamor blade. Nice sword!

Regards,
Detlef

[CharlesS]

Originally Posted by asomotif

Finally took some pictures with acceptable daylight of a peudeung from my own collection. Scabbard leather over wood.
Blade is laminated, What would you call this blade ?

Best regards,
Willem

Really attractive patter welding there Willem...consistent and good contrast. Is this the original etch or a later one?

[asomotif]

Originally Posted by CharlesS

Really attractive patter welding there Willem...consistent and good contrast. Is this the original etch or a later one?

Hello Charles,

I did not etch it myself.
The blade was pretty much in this condition when I bought it.

Best regards,
Willem

[CharlesS]

Originally Posted by asomotif

Hello Charles,

I did not etch it myself.
The blade was pretty much in this condition when I bought it.

Best regards,
Willem

That's even better. VERY nice!

[scinde]

Hi,

Quite new to this group, and not exactly a reply, but I would appreciate knowing the best method or process of testing a blade, to establish whether it is patterned or just plain. Thanks in advance.

Gordon

[ariel]

There is only one way: etch it. If there is a pattern, it is "pattern welded" ( or wootz), if not, - it is monosteel.

[scinde]

Hi Ariel,

Thanks for reply. I basic terms I was aware of the fact that the surface of the blade must be etched to reveal the grain structure however, the main thrust of my question was in relation to how the blade should be prepared for etching, and what chemicals or agents should be used to etch the metal.

Gordon

[Roland_M]

Originally Posted by scinde

Hi,

Quite new to this group, and not exactly a reply, but I would appreciate knowing the best method or process of testing a blade, to establish whether it is patterned or just plain. Thanks in advance.

Gordon

Hi Gordon,

a cheap and simple way to test a blade is to hold it under hot running water (must be hot enough, to burn your hand). If it is mechanical damascus, one can recognize the structure clearly after a few seconds.

Roland

[scinde]

Originally Posted by Roland_M

Hi Gordon,

a cheap and simple way to test a blade is to hold it under hot running water (must be hot enough, to burn your hand). If it is mechanical damascus, one can recognize the structure clearly after a few seconds.

Roland

Hi Roland,

Very interesting and helpful; it seems a combination of heating the blade with hot water and applying the vinegar solution will produce the desired result if there's anything to be seen.

Thanks for this additional information.

Regards,

Gordon