Arsenic or realgar for Keris etching?

[David]

Originally Posted by kulbuntet

I do hsare your opinion about that diffrent blades (pamor technices+material) need diffent aproach. Yes a new blade with pamor neckel/nickel/titanium or something that is pure. Needs a more stong solution, now since that AsS or As2S3 do not solve as good than As2O3(20Gr/l) And trioxide is wtronger to react.. beter to use trioxide. But with old blades as pamor Luwu and Pramamban beter to use less strong solution, realgar does the job good engouh. Just need to give it more time.

Just a thought. Can't the strength of the solution be adjusted based on the amount of arsenic used in the solution. As2O3 is stronger than realgar, but if you use less in your solution than your solution should be weaker, right?
Thanks for showing us part of your process Michel. I like your home made staining trough. Frankly i am picking up a tip or two from all these different methods which i believe will be helpful to my process in the end.