Meteoritic material is not hard to work, it is no more difficult to work than ordinary iron, but as I explained, if you do not take the very first weld very gently it will break up under the hammer, so the first weld is taken as gently as possible, and you need to bring the pieces to be welded, together in the forge, if you have more than a single piece of material, after that first weld, the following welds are easier and towards the end of the cleaning process, it is just like welding ordinary iron.

Pure nickel welded together with iron is also easy to weld, but when you want weld steel, say a simple high carbon steel like 01, together with iron, or with iron and nickel, you have a quite small weld window, so you need to be able to judge the weld temperature pretty accurately.

Material that is hot short is perhaps more difficult to weld that meteorite, but again, it is a matter of taking the first couple of welds very gently, as you get more welds into the billet you wash out more of the impurities and it becomes easier to weld.
A. G. Maisey is offline   Reply With Quote