Sword Construction - iron tangs.
Apologies if this subject has been covered in previous threads but as a relative newcomer I find some aspects of sword construction confusing and not well covered in the books.
For example why are iron tangs hammer welded to steel blades - does this not create a weak point?
Sometimes a faint line offset on each side or a difference in corrosion or even on shiny blades occasionally a difference in shine can be noted which indicates a scarf/lap joint on the blade a few inches from the hilt. At first I wondered why the original bar was just not made a little longer to avoid a join.
Am I correct in assuming that this is often where the iron starts? Is this primarily a European method?
Any information appreciated. CC.
|