The blade's edge was not ground down or the tip reprofiled. The nicks in the blade as well as the broken tip were welded back by the use of both mig and tig welding and the use of heatsink paste. As I have already promised Detlef a line drawing showing how this was accomplished if anyone else is interested I will also post the drawing here as well. Please remember this procedure it not one to be taken on by anyone who is not an accomplished welder in both methods that I have mentioned and can easily result in damaging the blade even more or its complete ruin if not done properly. Thank you all for your kind words in reference to my work.
Best,
Robert
|