Quote:
|
Originally Posted by Moshah
Looking at it, definitely the edge was heavily corroded. To commissioned a reworking is a futile effort, I afraid, as the sewar's edge would be taken away too much from its original body, and that would not proportioned with the thick spine.
The hilt, FYI, was a white akar bahar. And I am also in the thinking that it is new and I believe you are right.
But then again I would like to ask, is the polished form (the clean, steel looks) is really a desirable state on any sewar? I've seen numerous examples on the net was in that state...
|
Hello Moshah,
don't be afraid to do it byself, I have done it several times. Use sandpaper, first maybe 400 and go down to 1000 but do it with oil, you only get dirty fingers by this. After you have removed the corrosion etch it with hot vinegar. The complete procedure will take some time but is worth the effort. By this you can carefully reshape the edge also.
Regarding the hilt material I would say what I can see by your pictures that t is molar and not akar bahar.
Regards,
Detlef