Quote:
|
Originally Posted by Edster
I think in the included link the copper was pored rather than inlayed cold. Also, we have at least three kaskara with the same copper treatment into Kull swords, plus the takubas previously noted. This suggests to me a common source. It would have to be a shop capable of melting copper, likely a jewelry. Since we have takuba blades, maybe the shop was in Tunis, and your kaskara blade was traded into Sudan, likely Darfur. This is all speculation, but sounds reasonable.
A final question remains; WHY? Why would an importer or jeweler do this on a wholesale basis. Would potential purchasers consider them special?
|
Yes, it mimics European latten work on blade marks which I have detailed on various takouba before. Just two examples are attached.
I think as well it was likely done in bulk in a workshop for precisely this reason, as well as the talismanic properties