Quote:
|
Originally Posted by kai
Hello Detlef,
Congrats, you certainly did very well!
I also believe that there will be no twistcore - usually it should be discernible with this amount of corrosion. The remaining chance of twistcore would be if this blade (including fullers) got intensively buffed before long-time storage and the closed pores in the iron preventing the corrosion to show the pattern (can't see any hints though). Blade is definitely laminated, of course.
I hope you'll receive this in due time. I would certainly like to see the laminations after etching - it may help to verify wether this is an archaic kris or a later revival example. Anyway, the scrollwork at the base of the blade is very good quality.
Regards,
Kai
|
Hello Kai,
thank you! Will need a little bit time, the family in the States just have changed the room and don't have so much time in the moment.
And agree with you about the scrollwork, much better as by the other example I have.
Regards,
Detlef