Quote:
Originally Posted by Battara
I don't know Detlef, I kind of agree with Wayne. I have noticed that black oxidation is much more stable and have not had problems with it for years.
Now there is a point, however, that in order to get a proper etch for a pattern, you do have to remove the black oxidation as well.
|
Hi Jose,
It's chemistry, iron oxidation is always active, like said before, black oxidation isn't very fast but still active. It's different as aluminium oxidation which built a protection against further oxidation.
A proper etch of the blade could be worthwhile.
Best regards,
Detlef