Quote:
|
Originally Posted by Edster
I usually defer to Iain's superior knowledge and experience, but the blade doesn't necessarily look to me like a factory forged piece as would have been made in Solingen. It looks to be pretty (too?) thick for a few inches near the guard, but does appear to taper toward the tip. Is the blade stiff or flexible?
Also, the maker's marks and inscriptions are deep and don't appear to made into a hardened surface. Could the blade be made of a softer steel closer to wrought iron and produced outside a factory setting? Please correct me if my ignorance is showing.
Regards,
Ed
|
Hi Ed, I've seen 5 or 6 of these over the years, all of the same profile. Rudimentary to a degree, but cheap to knock out I'd imagine. The stamps would be done hot I believe.