Alan, thanks for that. I agree that unless you can see the pattern you cannot tell what the material is unless you do a in depth metallurgical analysis. Much like working wootz the pattern can disappear if heated to high. Makes you appreciate how good the ancient smiths where. For those wondering what it looks like here is a blade that appeared in Blade magazine, while not a keris it should give you an idea.
|