I've finally been able to get one of Jean's JPGs through Photoshop --- don't know why they wouldn't cooperate previously. Anyway, if you look at this pic you'll see the pamor grain comes to a peak just about where I've drawn a line, now look at the other side of the blade and you can see a lot of core material in this area of the blade.
Consider this:- take a nice little billet of gonjo material, weld it to one side of the blade and then even up the blade so that there is equal material on each side of a centre line. Result is you've got a thick little lump of material at the gandhik, so you then carve a puthut --- or whatever else you like--- into that thick little lump, but one side of the lump has pamor, the other side does not.
If the welded on lump is tapered down into the body of the blade it passes a cursory inspection as part of the original material.
|