Thanks for the feedback. Good to hear it isn't "abnormal". What caught my eye as unusual was the pronounced ridge line and secondly was how the blade was forged. It is not a layered or pamor blade. Rather, it is a homogeneous steel with hardened edges. If you look closely you can see the darkened zone along each edge. Curious how this would have been forged. But you are right David the lines are georgeous!
|