Yes Ann, I know, but I stand in a dilemma, should I really polish the blade up, or leave it as it is?
I have decided to leave it, although I have polished it quite a bit, as someone had treated it with acid, probably due to heavy rust. I would have been happier had he left it, then I would have cleaned it, but I am glad to say, that he left it to the blade, and did no harm to the hilt.
One thing important to notice is the ‘sound’ of a blade/hilt. It can tell you if it is forged or cast, but further more it can tell you if the blade is part broken, if you listen carefully enough. Try with some of your blades to hit them on wood or hard with a nail, and get used to the sound, suddenly you may find a blade with another sound – and this can be important, it can mean something –then look for the course to the different sound, and maybe you find, that something is not what you thought it was.
|