The lamination seems to remind me of shear steel I would not consider this blade a true pattern welded steel. If you take wrought iron and forge it to shape and etch it you will see the same pattern. My feeling is that this blade could have been forged from shear steel since it was exported all over the world by Britain during the late 1800s which is when I would place this daggers age.
Lew
|