Quote:
|
Originally Posted by Pukka Bundook
Roland,
You know more about this than I do, and cannot think I could add anything to what you describe above.
I did not know if all Indian barrels were etched, as I have a couple that are very smooth and uniform, and show no pattern either.
I should try an etch on a hidden area.
It appears I need more books! :-)
Steve,
That barrel is becoming very vibrant!
|
Hello Steve,
Her is the link to the "DamascusRestorationandRefinish.pdf" for you and add the link here in the thread. The results look very professional.
https://www.datafilehost.com/d/48547375
And another one about Barrel strength.
https://www.datafilehost.com/d/1b05bc93
If you try an etch on a hidden area, I would suggest a salt instead of acid, because it is less destructive. A mild solution of Iron(III) chloride (I dont like it but others got very good results with it) or Sodiumpersulfate (~10 grams on 100 millilitre distilled warm water (40-50°C), barrel should be warmed up with hot water from the water-tab). This is easy to remove without traces and brings out every tiny detail of the pattern. You can ask Sajen,in case you dont trust me.
Btw. it is hard to see from pictures but British barrels or European pattern welded barrels in generell seems to have no relief etching, only a staining.
It would be really interesting, to find out the true reason why Indian pattern welded barrels are deep etched? It could also simply be just a question of fashion.
More books are always good but I afraid, you will not learn more about restoration. What you need is a good validated guide. I hope "DamascusRestorationandRefinish" will help you, this guide has been done by pros.
Kind regards,
Roland