Hi Jean,
That's one nice keris. Congratulations. It's a pity it got broken like that. Nevertheless it is still a very handsome keris.
Quote:
Originally Posted by Bejo
Hello Jean,
But, when I examine the pamor from the top part. I have just realized that the pamor is not exceeding the edge of the wilah. Thats quite strange to me. From my opinion, it looks like the creator of top part has calculated so the pamor won't exceed it's edge.
|
Hi Bejo,
I think since the thickness of the blade towards the tip reduces after being reshaped, IMHO it is natural that the pamor does not exceed the wilah.
I once reshaped a broken tip of a keris. We can adjust the thickness when filing so that the pamor does not exceed towards the tip. If it is too close to the tip just file a bit more.
We just need to etch the blade a bit along the way so that we can see where the pamor is after each session of filing/grinding. Picture below is the reshaped tip before and after it was etched. We can see the pamor surfacing. (I think this pic is from different side though)