Quote:
Originally Posted by kai
Your blade does seem to be a genuine antique sewar. To be frank, the heavy pitting seems to be from excessive etching (and/or neglect). If it were not looking like a pretty much lost case, I would think about reworking/repolishing/staining the blade. I don't think this is feasible with this piece though.
The fittings (including the hilt) look newly crafted to me and may well be Malay "repair" attempts.
Regards,
Kai
|
Dear Kai,
Now I think I've got it right already.
Looking at it, definitely the edge was heavily corroded. To commissioned a reworking is a futile effort, I afraid, as the sewar's edge would be taken away too much from its original body, and that would not proportioned with the thick spine.
The hilt, FYI, was a white akar bahar. And I am also in the thinking that it is new and I believe you are right.
But then again I would like to ask, is the polished form (the clean, steel looks) is really a desirable state on any sewar? I've seen numerous examples on the net was in that state...